We are Manufacturer, Supplier & Exporter of Monel 400 Sheet & Plate (UNS N04400), Monel 400 Plates in various sizes, dimensions and standards at market leading prices. These Sheets & Plates from thickness 0.5mm in various pre-cut sizes from stock, Monel 400 Perforated Plate, Monel 400 Hot & Cold Rolled Sheets, Chequered Plates, Polished Sheets. If you do not find the size you are looking for or if you need Other Type of Sheets & Plate please do contact us
Specifications | ASTM B127 / ASME SB127, BS EN 10088-2, en 10028-7, IS 6911 |
---|---|
Dimension Standard | MSRR, AMS, BS, JIS, AISI, ASTM, GB, DIN, EN, etc |
Size Range | Cold rolled Plate 0.5-6.4 mm Hot rolled Plate 3.0–10.0 mm |
Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc |
Thickness | 0.3 mm to 120 mm |
International Standard | ASTM A480 ASTM A959 ASME IID EN ISO 9445 EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 |
Tolerances (width / thickness) | EN 10258/ DIN 59381) EN 10151 EN 10088 |
Finish | 2B, 2D, BA NO (8), Cold rolled Plate (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
Hardness | Half Hard, Soft, Hard, Quarter Hard, Spring Hard |
Value Added Service | Cladding, Heat Treatment, Annealed, Pickling, Polish, Rolling, Cutting, Bending, Forging, Minor Fabrication Etc. |
Dealers & Distributor of | SAIL, ESSAR, JINDAL, TATA, BHUSHAN, INDIAN, POSCO, JISCO, TISCO, LISCO, BAOSTEEL IMPORTED material |
Profiling | Plasma Plate Cutting Laser Plate Cutting Oxy-propane Flame Cutting |
STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
Monel 400 | 2.4360 | N04400 | NW 4400 | NA 13 | МНЖМц 28-2,5-1,5 | NU-30M | NiCu30Fe |
Grade | C | Mn | Si | S | Cu | Fe | Ni |
Monel 400 | 0.30 max | 2.00 max | 0.50 max | 0.024 max | 28.00 – 34.00 | 2.50 max | 63.00 min |
Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
Monel 400 | 8.8 g/cm3 | 1350 °C (2460 °F) | Psi – 80,000 , MPa – 550 | Psi – 35,000 , MPa – 240 | 40 % |